High Absorption Reduced Cladding (HARC) Erbium Doped Fibers

For mini, micro and pluggable QSFP EDFAs

  • Reduced cladding diameter for increased flexibility and improved mechanical reliability
  • Small coating diameter for a reduced coil stack size
  • High erbium doping level for shorter fiber lengths
  • Increased numerical aperture (NA) for lower bend loss

Typical Applications:

  • Mini, micro and pluggable QSFP-style EDFAs
  • Ultra small fiber lasers
  • ASE light sources
  • Fiber Optic Gyroscopes (FOGs)
Comparison
I-15(980/80)HCI-25H(1480/80)I-40(1530/80)HCI-60(1530/80)HCI-80(1530/80)HC
Cut-Off Wavelength (nm)1200-1320900-10751200-13201200-13201200-1320
Numerical Aperture0.24-0.26≥0.300.24-0.260.24-0.260.24-0.26
Mode Field Diameter (μm)4.8–5.4 @1550nm3.8–4.7 @1550nm4.8-5.4 @1550nm4.8-5.4 @1550nm4.8-5.4 @1550nm
Absorption (dB/m) @1531nm27–33 @1531nm23–27 @1531nm40 @1531nm60 @1531nm80 @1531nm
Proof Test (%)2 (200 kpsi)1 (100 kpsi)2 (200 kpsi)2 (200 kpsi)2 (200 kpsi)
Attenuation (dB/km) @1200nm≤15≤30≤30≤30≤30
Polarization Mode Dispersion (ps/m)≤0.005≤0.005≤0.005≤0.005≤0.005
Cladding Diameter (μm)80 ± 180 ± 180 ± 180 ± 180 ± 1
Core Concentricity (μm)≤0.3≤0.5≤0.3≤0.3≤0.3
Coating Diameter (μm)170 ± 5160 ± 5135 ± 5135 ± 5135 ± 5
Coating TypeDual Layer AcrylateDual Layer AcrylateDual Layer AcrylateDual Layer AcrylateDual Layer Acrylate
Operating Temperature (ºC)-55 to +85-55 to +85-55 to +85-55 to +85-55 to +85